Title 2303 マグネシウム合金の初期微小疲労き裂成長挙動に及ぼす結晶方位の影響(S07-1 マグネシウム合金の疲労,S07 構造 材料の疲労強度とき裂進展問題)( 本文(Fulltext) )
Author(s) 植松, 美彦; 杉江, 俊幸; 戸梶, 惠郎
Citation [年次大会講演論文集 : JSME annual meeting] vol.[2007] no.[1]p.[323]-[324]
Issue Date 2007-09-07
Rights Japan Society of Mechanical Engineers (日本機械学会)
Version 出版社版 (publisher version) postprint
URL http://hdl.handle.net/20.500.12099/25617
The Japan Society of Mechanical Engineers
The Japan Society of Mechanical Engineers
関連したドキュメント
本研究は，地震時の構造物被害と良い対応のある震害指標を，構造物の疲労破壊の
The larger the amount of Co in the three alloys is, the higher the dislocation density in the alloys peak-aged and rolled to a 25% and a 90% reduction is. The amounts of
Fig, 1.5 Comparison between result of plastic strain field by crystal plasticity FEA and fatigue test on crack initiation s ite in Ni alloy, a mapped region showing the grain
To accomplish the aim, the following investigations has been conducted; 1 explication of dominant factor determining fatigue crack initiation life in practical high strength
目的 今日，青年期における疲労の訴えが問題視されている。特に慢性疲労は，慢性疲労症候群
目的 青年期の学生が日常生活で抱える疲労自覚症状を評価する適切な尺度がなく，かなり以前
4 アパレル 中国 NGO及び 労働組合 労働時間の長さ、賃金、作業場の環境に関して指摘あり 是正措置に合意. 5 鉄鋼 カナダ 労働組合
⑥法律にもとづき労働規律違反者にたいし︑低賃金労働ヘ